POM Sheet

• Customization: Available
• Material: POM
• Kind: Engineering Plastic Sheet
• Model NO.: thickness 1mm to 100mm
• Contraction Percentage: ＜0.4%
• Tensile Strength: 51~80MPa
• Transport Package: Wooden Box
• Trademark: PEPSON
• Origin: China
• HS Code: 6801000000

Product Description

Polyoxymethylene sheet and rod is extruded by POM material under high temperature.  It is with high melting point and high crystallinity. Due to POM with excellent performance, it is very suitable for auto lathe machine to reprocess.  It could be reprocessed to precision parts perfectly.  POM is with high mechanical strength, rigidity, high hardness, good elasticity, good slip and abrasion resistance. Even under low temperature, it is also with high impact resistance, excellent dimensional stability, mechanical properties, and physical inertial, suitable to contact with good.  
     It is widely used in Auto, electronic, clothing, medical, machinery  and sports equipments as sliding parts, precision parts, gears , bearings etc.  

POM Sheet Size:
Thickness*width*length: 0.5mm*100mm*510/610mm*1000/2000mm
POM Rod: Diameter*length:  3mm-300mm*1000mm  
 

ITEM	METHOD	UNIT	VALUE
Mechanical Properties
Specific gravity	ASTM D792	g/cm3	1.46
Tensile yield strength	ASTM D638	Mpa	64
Breaking elongation	ASTM D638	%	20
Bending strength	ASTM 790	Mpa	84
Flexural modulus	ASTM 790	Mpa	2800
Shore hardness	ASTM D2240	D	85
Impact strength	ASTM D256	J/M	50
Thermal Properties
Melting point	DSC	ºC	190
Heat distortion temperature	ASTM D648	ºC	130
Operating temperature	-	ºC	100
Maximum operating temperature	-	ºC	150
Thermal conductivity	DIN 52612-1	W/(K-M)	0.33
Coefficient of linear thermal expansion	ASTM D696	10-5-1/K	1.3
Electrical Properties
Dielectric strength	ASTM D150	KV-mm	-
Dielectric loss factor	ASTM D150	-	-
Volume resistivity	ASTM D257	Ω.cm	10^14
Surface resistivity	ASTM D257	Ω	10^16
Dielectric constant	ASTM D149	-	-
Chemical Properties
Water absorption	23ºC 60%RH	%	0.5
Acid resistance	23ºC 60%RH		+
Alkali resistance			+
Acid and alkali resistance			+
Resistance to aromatic compounds			+
Resistance to ketone	23ºC 60%RH		+
Resistance to hot water	23ºC 60%RH		+
Others
Flammability	UL 94		HB
Viscosity	-		+
Non toxic	EEC 90/128 FDA		+
Coefficient of friction	DIN 53375		+
Anti-ultraviolet	-		0

Remarks:

1."+": positive "-": negative "0": depends.

2. All the parameters above are based on raw material but not finished products,